TECHNINIŲ DUOMENŲ LAPAS
Temaclad SC 50 - Acrylic polyurethane paint
|APIBŪDINIMAS||A two component, semigloss acrylic polyurethane with anticorrosive pigmentation. Hardener aliphatic isocyanate.|
|SAVYBĖS||Recommended to be used as a single coat finish for steel, aluminium and galvanized surfaces. Also suitable to be used as a topcoat in epoxy/ polyurethane systems. Not recommended for use in immersion conditions.|
|Paskirtis||Suitable for urban, marine and industrial environments.|
|Papildomos savybės||Outstanding colour and sheen retention. Tough, durable finish combining abrasion resistance with exceptional weathering properties, water and chemical resistance. Good cleaning properties.|
|Spalvų katalogai||RAL, NCS, SSG, BS, MONICOLOR NOVA and SYMPHONY colour cards. TEMASPEED tinting.|
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
|Skiediklis||1048 ir 1067|
|Maišymo santykis||Base 9 parts by volume 572-serie
Hardener 1 part by volume 008 7615
|Įrankiai||By airless or conventional spray (large surfaces) or by brush (small surfaces).|
|Mišinio tinkamumo trukmė (esant +23 ºC temperatūrai)||4 hours|
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
|Sausasis likutis||55 ± 2 % volume (ISO 3233)
69 ± 2 % weight
|Tankis||1.3 ± 0.1 kg / l (mixed)|
|Dengimo sąlygos||All surfaces must be dry. The temperature of the substrate should be above 0 °C and at least 3 ° above the dew point of the air. The temperature of the paint has to be over + 15 °C. If the temperature of the substrate is over + 50 °C, painting is not recommended. Good ventilation is required in confined areas to ensure proper drying. Condensation occurring during or immediately after application may result in matt finish and an inferior film.|
|Paviršiaus paruošimas||Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. (SFS-ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (SFSISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with PANSSARIPESU detergent.
Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with MAALIPESU detergent.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (SFS-EN ISO 12944-4)
Old alkyd and coil- coated ( not PVDF) surfaces: Remove rust and white rust by power tool cleaning to St 2. Hard, glossy paint surfaces should be roughened by abrading. Oil, grease, salt, dirt and dust are removed by washing with PANSSARIPESU detergent.
|Priming||TEMAPRIME EE and TEMACOAT GF. Suitable to be used without primer.|
|Viršutinio sluoksnio danga||TEMACLAD SC 50.|
|Dažymas||By airless or conventional spray (large surfaces) or by brush (small surfaces). In order to obtain an even, non-porous finish, spray a misty coat: first a thin layer, then let the solvents evaporate for 5 - 30 minutes and then apply the full coat. Depending on the application method and the temperature of the components (base, hardener, thinner) the paint can be thinned 0 - 10 %. Airless spray nozzle tip 0.011" - 0.015"; pressure 120 - 160 bar, spray angle shall be chosen according to the shape of the object. At brush application the paint should be thinned according to the circumstancies.|
|Komponentų maišymas||First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use a mechanical agitator for mixing. Insufficient mixing or incorrect ratio will result in uneven drying and weaken the properties .|
|Įrankių valymas||Thinner 1048 or 1067.|
|Lakiųjų organinių junginių kiekis (LOJ) (direktyva 2004/42/EB)||The Volatile Organic Compounds amount is 420 g/litre of paint mixture.
VOC content of the paint mixture (thinned 10% by volume) is 460g/l.
|SAUGOS IR SVEIKATOS APSAUGOS ŽENKLINIMAS|
pagal reglamentą EB Nr. 1272/2008
|Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.|