TECHNINIŲ DUOMENŲ LAPAS
04.11.2009

Temasil 90 - Silicate zinc-rich paint

 
Tikkurila Industry 9L
APIBŪDINIMAS A two component, ethyl silicate zinc rich paint.
SAVYBĖS Can be used as a single coat or as a primer in protective coating systems.
Paskirtis Recommended for bridges, pipework, heat exchangers and chemical tanks etc.

TECHNINIAI DUOMENYS
Papildomos savybės Offers cathodic protection of steel. Excellent resistance to abrasion and weathering. Excellent resistance also to high, dry temperatures up to + 480 ºC. Withstands immersion in oils and various solvents. Separate chemical resistance table available.
Spalva Greenish grey.
Blizgumas Matinis
Teorinė išeiga

Recommended film thicknesses

Theoretical coverage

dry

wet

 

60 µm

120 µm

9.2 m2/l

80 µm

160 µm

6.9 m2/l


Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Skiediklis 1029
Maišymo santykis Base 1 part by volume 008 7381
Hardener 1 part by volume 008 7380
Įrankiai By airless or conventional spray or brush.
Mišinio tinkamumo trukmė (esant +23 ºC temperatūrai) 5 hours
Džiūvimo laikas

DFT 75 µm

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

½ h

15 min

10 min

Touch dry, after

1 h

½ h

15 min

Recoatable, RH 85 % *see overleaf, after

36 h

5 h

2 h

Recoatable, RH 70 %, after

48 h

24 h

7 h

Recoatable, RH 50 %, after

-

48 h

24 h


Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Sausasis likutis 55 ± 2 % volume
Tankis 2.0 kg / l (mixed)
Gaminio kodas 008 7381

NAUDOJIMO INSTRUKCIJA
Dengimo sąlygos All surfaces must be dry. The temperature of the ambient air or surface should not fall below -15 ºC during application and drying. Relative humidity should be 50 - 90 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Paviršiaus paruošimas Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½ - 3. (ISO 8501-1)
Viršutinio sluoksnio danga Temachlor 40, Temacryl AR, Temacryl EA, Temal, Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat RM 40 and Temacoat SPA.

Temasil 90 may be overcoated with above mentioned paints when Thinner 1029 does not dissolve the coat. Before overcoating it is recommended to spray a misty coat with 25 % thinned Temacoat GS 50.
Dažymas By airless or conventional spray or brush. Agitate during application. Depending on the application method the paint can be thinned 0 - 5 % by volume. Airless spray nozzle tip 0.018" - 0.021" and nozzle pressure 120 - 180 bar. Spray angle shall be chosen according to the shape of the object.

When coating interiors of chemical tanks or working in dry conditions, it is recommended to rinse the paint film with fresh water 1 - 24 hours after application. Sharp edges, corners, weld seams and other areas difficult to cover properly by spray application should be coated by a brush before the spray application.

Note! There is a risk of mudcracking or peeling with heavier coats than approx. 100 µm dry film thickness.

Separate application instructions available.
Komponentų maišymas First stir base and hardener separately. The correct proportions of base and hardener must be mixed thoroughly before use. Use Temaspeed Squirrel Mixer for mixing.
Įrankių valymas Thinner 1029.
Lakiųjų organinių junginių kiekis (LOJ) (direktyva 2004/42/EB) The Volatile Organic Compounds amount is 470 g/litre of paint.
VOC content of the paint mixture (thinned 5 % by volume) is 480 g/l.

SAUGOS IR SVEIKATOS APSAUGOS ŽENKLINIMAS
pagal reglamentą EB Nr. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oy.
Saugos duomenų lapasTemasil 90
Skiediklio saugos duomenų lapasTHINNER 1029 [GB-ENG]
Kietiklio saugos duomenų lapasTemasil 90
 
-


Atgal