Tirpiklio pagrindu gaminami produktai

TECHNINIŲ DUOMENŲ LAPAS
15.10.2007

Temanyl PVB - Polyvinyl-butyral adhesion primer

APIBŪDINIMAS

A one component, polyvinyl butyral adhesion primer.

SAVYBĖS

An adhesion primer for steel, zinc, stainless steel and aluminium surfaces. Fast drying, can be applied using a "wet-on-wet" painting technique. Can also be used as a primer under powder coatings. For industrial use only according to Directive 1999/13/EC.

Paskirtis

Steel, zinc, stainless steel and aluminium surfaces.

TECHNINIAI DUOMENYS

Spalva

Grey, yellow and black.

Blizgumas

Matinis

Teorinė išeiga

Recommended film thicknesses		Theoretical coverage
dry	wet (unthinned paint)
10 µm	45 µm	23.0 m²/l
20 µm	90 µm	11.5 m²/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

Skiediklis

1031 ir 1112

Įrankiai

By airless or conventional spray or dip.

Džiūvimo laikas

DFT 20 µm	+ 10 ºC	+ 23 ºC	+ 35 ºC
Dust dry, after	20 min.	15 min.	5 min.
Touch dry, after	55 min.	45 min.	20 min.
Recoatable, min. after	20 min.	10 min.	5 min.
Through dry after 30 min. / 150 ºC

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.

Sausasis likutis

23 ± 2 % volume

Tankis

1.11 - 1.17 kg / l depending on the colour.

Gaminio kodas

007 4485 (18116), 007 4486 (18128) and 007 4488.

NAUDOJIMO INSTRUKCIJA

Dengimo sąlygos

All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below + 5 ºC during application or drying. Relative humidity should not exceed 80 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.

Paviršiaus paruošimas

Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN ZN detergent.

Stainless steel: Roughen the surface by grinding or sweep blasting using mineral abrasives.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN AL detergent.

Priming

TEMANYL PVB.

Viršutinio sluoksnio danga

DUASOLID, TEMATHERM AA 30, TEMATHERM AA 90 and TEMADUR.

Dažymas

By airless or conventional spray or dip. The application viscosity should be 20 s DIN 4. Airless spray nozzle tip 0.011"- 0.013 " and nozzle pressure 120 - 160 bar.

Note! When stoving Temanyl PVB before overcoating the temperature must not exceed 160 ºC because the intercoat adhesion may then deteriorate.

Įrankių valymas

Thinner 1031 or 1112.

Lakiųjų organinių junginių kiekis (LOJ) (direktyva 2004/42/EB)

The Volatile Organic Compounds amount is 690 g/litre of paint.
VOC content of the paint (thinned 30 % by volume) is 740 g/l.

SAUGOS IR SVEIKATOS APSAUGOS ŽENKLINIMAS
pagal reglamentą EB Nr. 1272/2008

Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Coatings Oy.

Saugos duomenų lapas

Temanyl PVB

Skiediklio saugos duomenų lapas

THINNER 1031 [GB-ENG]

Aukščiau pateikta informacija yra pagrįsta laboratoriniais bandymais ir praktine patirtimi, patvirtinta nuo datos, nurodytos produkto duomenų lape. Produkto kokybę užtikrina mūsų veiklos sistema, pagrįsta ISO 9001 ir 14001 reikalavimais. Gamintojas neatsako už žalą, patirtą naudojant produktą ne pagal instrukciją ar netinkamu tikslu.

Atgal