Fontecryl AP - Water-borne acrylic primer

APIBŪDINIMAS A waterborne, one component fast drying acrylic based primer containing active anticorrosive pigments.
SAVYBĖS Recommended to be used as an anti-corrosive primer on steel, aluminium and zinc surfaces. Suitable also for dipping. Drying times can be shortened by using higher temperatures. Overcoatable with a wide range of products, also with solventborne products.
Paskirtis Steel, aluminium and zinc surfaces.

Spalva Black, grey, yellow, iron oxide red, green, dark grey, RAL 8017 and TEMASPEED FONTE tinting..
Blizgumas Matinis
Teorinė išeiga

Recommended film thicknesses

Theoretical coverage




40 µm

125 µm

8.3 m2/l

Recommended film thicknesses with Duasolid 50 as a topcoat

Theoretical coverage




20 µm

60 µm

16.5 m2/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Skiediklis Vanduo
Įrankiai By spray or dip.
Džiūvimo laikas

DFT 40 µm

+ 15 ºC

+ 23 ºC

+ 60 ºC

Dust dry, after

2 h

30 min

5 min

Touch dry, after

2 ½ h

1 h

15 min

Recoatable , min. after

24 h

1 - 2 h

30 min

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Sausasis likutis 33 ± 2 % volume
Tankis 1.2 kg / l
Gaminio kodas 006 5970, -71, -72, -73, -74, -75, -76, 539-series

Dengimo sąlygos All surfaces must be dry. The temperature of the ambient air, surface or paint should not fall below +15 ºC during application or drying. Relative humidity should be between 20 - 70 %. The surface temperature of the steel should remain at least 3 ºC above the dew point.
Paviršiaus paruošimas Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Viršutinio sluoksnio danga DUASOLID 50, TEMADUR SC, FONTELAC QD 80 and FONTECRYL 50.
Dažymas By spray or dip. Depending on the application method the paint can be thinned 0 - 15 %. At dip application the viscosity should be 20 - 25 s DIN 4.

Note! The viscosity falls quickly when thinning the paint.
Įrankių valymas FONTECLEAN 1921.
Lakiųjų organinių junginių kiekis (LOJ) (direktyva 2004/42/EB) The Volatile Organic Compounds amount is 120 g/litre of paint.
VOC content in paint (thinned 15 % by volume) is 100 g/l.