Temafloor AC102 Primer - Solvent-free acrylic primer

Temafloor AC102 Primer
APIBŪDINIMAS A two-component, solvent-free low viscosity acrylic primer.

For impregnating of new and old concrete floors prior to laying Temafloor  AC coatings and screeds.

Cures fast also in low temperatures.

Paskirtis Used as a primer for Temafloor AC acrylic coatings and troweling screeds.

Spalva Sunlight will affect on the shade and the gloss of the varnish in the long run.
Blizgumas Pusiau blizgus
Teorinė išeiga

Coverage on concrete floors is on the average:


Primer coat                        2–2,5 m2/l


Practical coverage depends on the porosity and evenness of the substrate and on the application method.
Pakuočių dydžiai 200 l drum, content 180 kg
Įrankiai Temafloor AC102 Primer is applied with a roller or trowel.
Ypatinga savybė

Temperature (oC)*

The amount of hardener (percentage of weight of the binder)

Pot life (min)

Drying time (min)



ab. 8

ab. 30



ab. 8

ab. 30



ab. 7

ab. 30



ab. 8

ab. 30



ab. 7

ab. 30



ab. 6,5

ab. 30

* Temperature of the binder, air and the floor.

Possible hardeners:
BP-50-FT, Perkadox®CH-50 or PEROXAN BP-Pulver 50 W.

Sausasis likutis Approx.100 vol- %.
Tankis 1.0 kg / l (ready made mixture)
Gaminio kodas 001 6083

Dengimo sąlygos The relative humidity of the concrete should not exceed 97%. The temperature of the ambient air, surface or coating should not fall below +15ºC during application or drying. Relative humidity of air should not exceed 80%.
Paviršiaus paruošimas New concrete
Remove laitance by power grinding, vacuum grit blasting or hydrochloric acid etching. Choose the method best suited for the premises. After grinding remove dust carefully with a vacuum cleaner. Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water). Rinse with plenty of water. Dry the floor.

Old concrete
Remove all grease, oil, chemicals and other impurities by MAALIPESU detergent. Remove old peeling paint layer by grinding or vacuum grit blasting. Clean out pot-holes removing all loose friable material. Open cracks with e.g. an abrasive tool. Remove loose material and dust.
Gruntavimas Prime using Temafloor AC102 Primer. Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface. If necessary, repeat priming to get a non-porous surface. Subsequent treatment can be carried out after 30 min.

Scatter sand of grain size 0.4–0.8 mm on the fresh primer coat to ensure the screed adhesion and prohibit gliding of the screed.
Glaistymas Patch pot-holes and cracks with a mixture of unthinned Temafloor AC102 and dry, clean sand. Mixing ratio e.g. 1 part by volume of varnish mixture and 1–2 parts by volume of sand of grain size 0,5–1,2 mm.

The floor can be levelled by using Temafloor AC102 Primer and sand of grain size 0,1–0,3 mm.
Skiedimas Do not thin.
Dengimas Coating or screeding may be carried out after the primer has cured. A porous primer coat will result in holes and air bubbles in the finished coating.
Komponentų maišymas Mix the correct proportions of base and hardener powder thoroughly (approx. 2 minutes) by using an industrial hand drill with a paddle. The amount of mixture depends on the area to be coated and on the pot life of the mixture. Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the primer and risk the success of the application.
Įrankių valymas Cleaning of equipment with Thinner 006 1400.
Lakiųjų organinių junginių kiekis (LOJ) (direktyva 2004/42/EB) VOC 2004/42/EC (cat A/j) 500 g/l (2010)
Temafloor AC102 Primer: max. VOC < 500 g/l.

pagal reglamentą EB Nr. 1272/2008
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets. A health and safety data sheet is available on request from Tikkurila Oyj. For professional use only.
Saugos duomenų lapasTEMAFLOOR AC102 PRIMER en

CE logo
EN 13813
Adhesion after thermal compatibility